Hot Press Type HP W
Brand: FCT Systeme | Category: Nanotechnology
A resistance heated uniaxial vacuum hot press for compacting powders and powder compacts under combined temperature and pressure. It consolidates composite materials and technical ceramics in graphite moulds under vacuum or inert gas.
Technical Specifications
| Parameter | Value |
|---|---|
| Working temperature | up to 2200 deg C, optionally 2400 deg C |
| Maximum temperature in air | 1400 deg C |
| Specification | Models HP W 10 to HP W 400-SP, pressing force 100 kN to 4000 kN |
| Maximum pressing diameter | 60 mm to 680 mm |
| Maximum heating power | 30 kW to 350 kW |
| Specification | Vacuum 5x10-2 mbar(a), furnace atmosphere argon or nitrogen |
Get a Quote
Request an itemised quotation covering the proposed configuration, availability, lead time and agreed supply and support scope.
Useful details to share
- Materials, sample dimensions and process or measurement goal
- Required performance and existing instrument interfaces
Share what you know. You can start with your name and a phone number or email; final specifications can follow.
Not sure which configuration you need? Help me choose
Contact Vvon Technologies Limited about FCT Systeme equipment requirements in Bangladesh.
Phone: +8801805987890 | Email: info@vvon.com.bd
More from Furnaces & Sintering Systems
- Multi-purpose Hot Press HP P
A resistance heated hybrid press that combines classic uniaxial hot pressing with gas pressure sintering in one chamber. It is used for hot pressing, vacuum sintering and pressure sintering during materials development on samples up to 80 mm diameter.
- Carbon Fibre Heat Treatment Furnaces
Custom furnaces for carbon fibre research and production, covering the three stages of the process. Precursors are debound in a metal work tube, pre-sintered in a ceramic work tube, then finally sintered in a water cooled graphite heated vessel.
- High Temperature Vacuum Sintering Furnace Type FH W
A horizontal, resistance heated vacuum sintering furnace with a swivel door. It is used for debinding and subsequent sintering of ceramics, composites and powder metallurgical parts, and for carbonisation, silicon infiltration, nitriding and metallisation.